Preparation and Characterization of Mn doped NiCuZn Ferrite
Author Affiliations
- 1Azad College, Ausa, Dist Latur, MS-413520 INDIA
Res.J.chem.sci., Volume 3, Issue (11), Pages 32-35, November,18 (2013)
Abstract
The ferrite composition [Ni0.25-xMn.xCu.2Zn0.55] Fe2O4 with values x= 0.00, 0.05, 0.1 were synthesized by auto combustion method. XRD analysis of prepared ferrite powder shows the cubic spinal structure. The crystallite size of prepared ferrite is varied from 22.3 to 39.3 nm the resultant powder were calcined at 650°C/2hr and the pressed ferrite were sintered at 950°C/4hr the initial permeability, dc resistivity were measured with frequency range 100Hz to 5MHz. The permeability is found to be increase up to x=0.1 and dc resistivity was decreased with Mn Substitution. The very high permeability in the composition x=0.1 was due to better densification and lower magnitostriction constant. The lattice parameter are also slightly increases from x=0 to=0.1. The composition is better than the NiCuZn based material. It is useful for Multilayer chip inductor.
References
- Nakamura T., J. Magn.Magn.Mater., 168, 285 (1997)
- Fujimoto M., J. Am Ceram.Soc., 77(11), 2873 (1994)
- Ayoma T., Hirota K. and Yamguchi O., J Am ceram.Soc., 79(10), 2792 (1996)
- Dione G.F. and West R.G., J.App.phys., 81(8) 4794 (1997)
- Wang S.F., Wang Y.R., Thomas C.K., Yang P.J., Wang C.A., Lu, J.Magn. Mater, 217 (2000)
- Magn.Mater. 251 (2002) 316-322Xi-Wei Qi, Ji Zhou, Zhenxing Yue, Zhi-Lun Gui. Long-Tu Li,J. Magn. (2002)
- Ranga Mohan G., Ravinder D., Raman Reddy A.V., Boyanov B.S., mater.Lett.,40, 39 (1999)
- Snelling E.C., Soft Ferrite, 2nd ed. Butterworths, London (1988)
- Rosales M.I., Cuautle M.P. and Castano V.M., J. Mat.Sci.,33, 3665.3669 (1998)
- Zhen-Xing Yue, Ji Zhou, Long – Tu Li, Xia ohui wang. Zhilum Gui, Mater. Sci. Eng., B 86, 64-69 (2001)
- ElHiti M.A., J. Magn.Magn. Mater., 136, 138 (1994)
- Parvatheeswara Rao B. and Rao K.H., J. Mater.Sci., 32, 6049 (1997)
- Liu D.M., J.M ater.Sci., 29, 1507 (1994)
- Valenzulla R., magnetic ceramics, Cambridge, (1994)
- Watawe S.C., Sarwade B.D., Bellad S.S., Sutar B.D. and Chagula B.K., J. magn.magn mater., 214, 55 (2000)