Research Journal of Chemical Sciences ______________________________________________ ISSN 2231-606X Vol. 4(5), 1-9, May (2014) Res. J. Chem. Sci. International Science Congress Association 1 Synthesis and Characterization of Poly Acrylic Acid Modified with Dihydroxy Benzene-Redox PolymerV. Vetriselvi and R. Jaya Santhi R* PG & Research Department of Chemistry, Auxilium College, Vellore, Tamil Nadu, INDIA Available online at: www.isca.in, www.isca.me Received 30th November 2013, revised 25th January 2014, accepted 29th April 2014Abstract Poly acrylic acid was functionalized with catechol, hydroquinone, catechol-hydroquinone, a homolytic modification by an oxidative decarboxylation using ammonium persulphate as an oxidant. The chemically modified PAA/Catechol, PAA/Hydroquinone and PAA/Catechol-Hydroquinone were characterized using UV and FT-IR. Thermal analysis shows PAA/Catechol, and PAA-Hydroquinone are stable above 700C and their Ea are lesser for PAA/Hydroquinone with the highest percentage of substitution than the other two polymers. The kinetic parameters were calculated from the TGA curves and the average molecular weight measured by viscometer was found to be around 1.1X10g/mol. From XRD studies the prepared polymers were found to be semi crystalline nature which is confirmed from the SEM analysis. The morphology of the redox polymer was found to be rod and cage like microstructure. From the CV studies, the potential difference was calculated. Keywords: Polyacrylic acid, Catechol, Hydroquinone, Redox polymer, Mid potential. Introduction Polymers can be prepared through various techniques such as radical, cationic and anionic polymerization1-6. The mechanical, thermal and structural properties can be studied through different kinds of characterization methods to determination of structure–property relationships7,8. Recently, polymers have been applied in various fields such as automotive, construction, electronic, cosmetic and pharmaceutical industries due to its advantageous material properties. Functional polymers of controlled refractivity, photochromic10 electrochromic11 and optoelectronic12 functions were developed recently. The use of polymers with tunable refractive properties as optical modulators, optical filters, or electro optic waveguide devices has been reported13. The functionalization of bioactive molecules can be carried out due to presence of carboxylic groups in Poly Acrylic Acid. The interactions due to the electrostatic forces, hydrophobic nature, hydrogen bonding, vanderwaals forces or the combination of these interactions leads to the formation of polymer complexes. The formation of complexes may strongly affect the polymer solubility, rheology, conductivity, and turbidity of polymer solutions, mechanical properties permeability, electrical conductivity of the polymers. Particularly, polyelectrolyte complexes are formed by the reaction of a polyelectrolyte with an oppositely charged polyelectrolyte in an aqueous solution. Electrostatic interactions are considerably stronger than most secondary binding interactions. Thus, electrostatic polyelectrolyte complexes exhibit unique physical and chemical properties with reasonable biocompatibility14. Stability of the complex is influenced by the polymer composition and structure, as well as by hydrophobic interactions. In addition, stability of the complex is dependent on many environmental factors, such as temperature, the nature of the solvent, pH, or ionic strength. The polymers with redox entities can act as redox agents, corrosion inhibitors, super adsorbent and metallic adsorbents15,16. The metallic adsorption is through their chelating ability17. The other feature of these molecules is their phenolic nature, implying a unique chemistry18. In the present work a homolytic modification by decarboxylation of PAA modified with catechol, hydroquinone and catechol-hydroquinone was synthesized. Material and Methods The chemicals were purchased from Merck. The viscometric measurements were performed in dioxane at 30C using Cannon Ubbelohde capillary viscometer. The average molecular weights (Mw) were estimated by the standard relation of Mark–Houwink–Sakurada19,20. UV–Vis spectra were recorded using a UV–Vis spectrophotometer Systronics 34215. Infrared spectra were taken with a Bruker FT-IR. X-ray diffraction measurement was carried out using Diffractometer system XPERT-PRO with Cu K radiation ( = 0.154 nm) at the scanning rate of 2°/min. The average crystallite size was calculated from the Scherrer's formula21. The SEM of polymer samples has been scanned at 12000X magnification by FEI Quanta FEG 200 High Resolution SEM. The thermal studies were carried out on SDT Q600 V8.3 build 101 with the heating rate of 10C min-1 under nitrogen atmosphere and Ea were calculated from the thermograms using Sharp-Wentworth, Freeman-Carroll methods22. Synthesis and Chemical modification of poly acrylic acid: Poly acrylic acid (PAA) was synthesized through a radical polymerization using hydrogen peroxide23 as radical initiator Research Journal of Chemical Sciences ___________________________________________________________ ISSN 2231-606XVol. 4(5), 1-9, May (2014) Res. J. Chem. Sci. International Science Congress Association 2 and chemically modified using ammonium persulphate as an oxidant. An aliquot from the reaction mixture was taken at the end of each hour and the absorbance value was observed to calculate the percentage of substitution24,25. Results and DiscussionDegree of substitution: The degree of substitution of dihydroxybenzene in PAA increases with time. It is because the dihydroxybenzene moieties gradually increase with the removal of the carboxylic group present in the PAA figure-1. At the end of 7th hour, the degree of substitution was found to be 84%, 91% and 87% for modified PAA/CAT, PAA/HQ and for PAA/CAT-HQ. The higher substitution in PAA/HQ is also proved by the lower Ea values. UV FT-IR spectra: The absorption bands of poly acrylic acid at 264 nm is due to n* transition of and the band at 365, 296 and 288 nm in chemically modified poly acrylic acid with catechol, hydroquinone and catechol-hydroquinone is due to * transition 26 and the corresponding spectra are given in figure-2. FT-IR spectra: The FT-IR spectra of the PAA and PAA modified with catechol/Hydroquinone and catechol-hydroquinone are presented in figure-3. Due to the incorporation of the dihydroxybenzene moieties into the poly acrylic chain the intensity of the acid O–H stretching band was enhanced around 3500cm-1. A shoulder-looking band around 1300-1400 cm-1 is assigned to O–H deformation vibration mode of the dihydroxybenzene. When compared with PAA there exists a broadening at 1625 and 1800 cm-1 due to substitution of the aromatic group. The presence of band at 755, 876, and two bands at 755 and 857 confirms the presence of catechol, hydroquinone and both catechol and hydroquinone moieties attached to the PAA chain27. Molecular weight: The average molecular weight of PAA, PAA/CAT, PAA/HQ and PAA/CAT-HQ are represented in the table-1. The intrinsic viscosity () Voluminosity (Ve) and the simha shape factor () 24,28 were calculated. The simha shape factor value was approximately 12.5 shows asymmetric prolate ellipsoid shape29 for the macromolecules. The table clearly illustrates that as theintrinsic viscosity increases the molecular weight increases in the case of PAA/HQ and the polymer exists in an elliptical shape with rod like arrangement in solutions. It is observed that as the percentage of substitution increases, the average molecular weight also increases linearly from pure PAA to chemically modified PAA. The higher branches and longer chain lengths of PAA on the backbone of PAA leads to the higher molecular weight of the chemically polymer30. X-Ray Diffraction studies: The XRD spectra of PAA and chemically modified PAA are given in figure-4 and different parameters calculated from the spectra are presented in table-2. The poly acrylic acid is amorphous in nature, whereas in the chemically modified PAA/CAT found to have a small peak at 16.3°, d-spacing 5.40628Å, with the crystalline size of 0.70 nm. The 100% relative intensity exists at 23.5° and 65.3° with the d spacing of 3.77695Å, 1.42871 Å with the crystalline size of 0.33nm and 0.54nm for PAA/HQ and PAA/CAT-HQ. From the XRD studies it was confirmed that the synthesized chemically modified polymer exhibits polycrystalline nature which is evident from the sharp peaks31. Figure-1 Effect of time on the percentage of substitution in chemically modified PAAs Research Journal of Chemical Sciences ___________________________________________________________ ISSN 2231-606XVol. 4(5), 1-9, May (2014) Res. J. Chem. Sci. International Science Congress Association 3 a. PAA b. PAA/CAT c. PAA/HQ d. PAA/CAT – HQ Figure-2 UVspectra of PAA and Chemically modified PAA a. PAA b. PAA/CAT c. PAA/HQ d. PAA/CAT – HQ Figure-3 IR spectra of Poly Acrylic Acid and Chemically modified Poly Acrylic AcidsTable-1 Comparison of Molecular weight, intrinsic viscosity, Voluminosity, Shape factor of PAA and chemically modified PAA at 30C Polymer dlg - 1 Mw(g/mol) (Ve) () PAA 0.58 5.8x10 5 0.06 9.6 PAA/CAT 0.74 9.3 x10 5 0.05 12.3 PAA/HQ 0.77 1.01x10 6 0.06 15.4 PAA/CAT-HQ 0.75 9.6x10 5 0.05 12.5. Table-2 XRD data for the calculation of crystalline sizePolymer 2 (°) Height [cts] FWHM Left (°) d-spacing [Å] Rel. Int. [%] Crystallite size (nm) PAA/CAT 16.3830 30.21 0.6000 5.40628 100.00 0.69803 23.5555 44.36 0.5904 3.77695 100.00 0.333287 25.1190 7.64 0.5904 3.54530 17.23 0.234914 PAA/HQ 35.7939 4.09 0.4920 2.50869 9.22 0.486385 51.9364 10.85 0.5904 1.76065 24.46 0.350172 60.2254 7.73 0.5904 1.53664 17.42 0.888498 77.3485 2.13 0.5904 1.23371 4.81 0.418692 PAA/CAT-HQ 60.0376 1.71 0.5904 1.54100 20.62 1.359439 65.3134 1.21 0.7872 1.42871 14.60 0.543661 Research Journal of Chemical Sciences ___________________________________________________________ ISSN 2231-606XVol. 4(5), 1-9, May (2014) Res. J. Chem. Sci. International Science Congress Association 4 a. PAA b. PAA/CAT c. PAA/HQ d. PAA/CAT – HQ Figure-4 XRD of PAA and chemically modified Poly Acrylic AcidSEM Analysis: The SEM images from the figure-5 shows PAA has lamellar arrangement with amorphous surface nonporous solid microstructure and for PAA modified with catechol shows bird nest like polymeric arrangement. The SEM micrograph for the polymeric intermediate prepared with chemically modified PAA/HQ showed polymeric solid structure with big voids and this may be due to the functionalization of hydroquinone moiety into the poly acrylic acid matrix. The better polymerization in PAA/HQ is consistence with FT-IR, XRD and the highest percentage substitution UV absorbance studies. The polymeric flakes with large number of micro voids exists a porous nature in PAA/CAT-HQ32. Thermo Gravimetric Analysis studies: The Thermo Gravimetric Analysis of the prepared polymers is presented in figure-6 and in the three chemically modified PAA namely PAA/CAT, PAA/HQ and PAA/CAT-HQ, the first degradation peak is due to the radical transfer occurred at 150°C. After the H–H scission, some termination occur leading to unsaturated ends which degrades around 270°C. The third step was due to the degradation initiated by the radical transfer to the unsaturated ends formed in the second stage. Since there is no simultaneous decrease of the second and third transition no coupling took place and the fourth transition occurred at 600°C would correspond to the random scission of the polymeric chains. The side-chain elimination could not be an initiation route for depropagation because of the amount of chars produced33. It is noticed that for the chemically modified PAA studied in the present work, the amount of char did not exceed to1% in the case PAA/HQ, PAA/CAT-HQ but in the case of PAA/CAT the char was found to be 1.79%. The char obtained substantiates that the initial route for depropagation took place without the side chain elimination. The activation energy calculated from the TGA curve for PAA and chemically modified PAA are found to be 13.42, 11.26 and 13.09 KJ/mol by Sharpwent Worth method and 17.06, 15.5 and 16.5 KJ/mol by Freeman Carroll method for PAA/CAT, PAA/HQ and PAA/CAT-HQ. The various kinetic parameters represented in the table 3, calculated by Freeman-Carroll method are about same, indicating common mode of decomposition reaction. The plots of Sharp Wentworth method and Freeman-Carroll method are represented in the (figure-7, 8, 9). Abnormally, the low values of frequency factor may be indicated that the decomposition reaction can be classed as slow reaction. The slow reaction is also predicted by negative values of entropy change. The negative values indicate that the disorder is less and the reaction is carried by more orderly manner, making it slower. The graphs obtained by Sharp-Wentworth and Freeman-Carroll methods are liners by ignoring some abnormal points, indicating that the decomposition does not obey first order kinetics. The comparative parameters of Ea, free energy change and frequency factor show that PAA/CAT is found to be thermally more stable than the PAA/HQ and PAA/CAT-HQ34. Differential Scanning Calorimetry Studies: The different phase temperature was observed from DSC curve figure-10 The DSC curve of unmodified PAA, the Tg was observed at Research Journal of Chemical Sciences ___________________________________________________________ ISSN 2231-606XVol. 4(5), 1-9, May (2014) Res. J. Chem. Sci. International Science Congress Association 5 127°C35. Upon modification with PAA/CAT, PAA/HQ and PAA/CAT-HQ, the Tg of PAA/HQ increases gradually with increasing HQ content. It also indicates that original carboxylic acid association could be a main factor to keep a relatively higher Tgin unmodified PAA. The Tg of PAA/CAT was 88°C , and an endothermic peak at 419°C was observed related to crystalline temperature (Tc) with the H of 904.4 J/g. The exothermic peak at 686 °C correlates with the melting temperature (Tm) of the polymer and has the H value of 161 J/g. The Tg of chemically modified PAA/HQ was 159°C with the H of 105.9 J/g, the Tc 323°C with the H of 291.1 J/g, and Tm was 448°C with H of 146 J/g. In the case of PAA/CAT-HQ, the second endothermic peak appeared at 281°C with the H= 136.6 J/g which corresponds to the Tc. The absence of endothermic peak in PAA/CAT-HQ after 323°C relates to the lack of melting process of the crystalline fraction which further confirms the presence of strong interactions between the polymeric back bone and the aromatic moiety36. Table-3 Kinetic parameters calculated from the Thermogravimetric analysis Polymer Half decomposition temperature (K) Ea (KJ/mol) Entropy Change S(J) Free Energy change F(KJ) Frequency Factor (sec) Apparent Entropy Change S* Order of reaction found (n) Freeman- Carroll method Sharp-Wentworth method PAA/CAT 573 17.06 13.42 -277.6 230 181 -55.78 1.2 PAA/HQ 583 15.59 11.26 -266.5 190 166 -55.89 1.4 PAA/CAT-HQ 553 16.51 13.09 -229.6 194 96 -56.11 1 a. PAA b. PAA/CAT c. PAA/HQ d. PAA/CAT – HQ Figure-5 SEM images of of PAA and chemically modified Poly Acrylic Acids a. PAA/CAT b. PAA/HQ c. PAA/CAT – HQ Figure-6 TGA of Chemically modified Poly Acrylic Acids Research Journal of Chemical Sciences ___________________________________________________________ ISSN 2231-606XVol. 4(5), 1-9, May (2014) Res. J. Chem. Sci. International Science Congress Association 6 Figure-7 Sharp-Wentworth plot of PAA/CAT Figure-8 Thermal activation energy (Freeman- Carroll) plot of PAA/CAT Figure-9 Freeman-Carroll plot of PAA/CAT Research Journal of Chemical Sciences ___________________________________________________________ ISSN 2231-606XVol. 4(5), 1-9, May (2014) Res. J. Chem. Sci. International Science Congress Association 7 Cyclic voltammetry studies: The cyclic voltammograms of the chemically modified PAA is given in figure-11 and their corresponding potential differences are presented in table-4. The well defined votammograms were obtained in the case of PAA/CAT. In acidic medium, the current response with respect to the potential difference was quiet good when compared to the other electrolytes. This is due to the doping and de-doping of the ion in to the polymeric matrix coated over the electrode surface37. a. PAA/CAT b. PAA/HQ c.. PAA/CAT – HQ Figure-10 DSC of Chemically modified Poly Acrylic Acids a. PAA/CAT b. PAA/HQ c. PAA/CAT – HQ Figure-11 CV studies for chemically modified PAA with Catechol, Hydroquinone, Catechol-Hydroquinone with different electrolytes Table-4 Comparison of potential difference of chemically modified PAA Polymer Electrolyte (0.1M)pa (V)pc(V)DD (mmA) x10-5c mmA) x10-5 PAA/CAT HCl 0.5516 0.4623 0.0893 -2.051 1.429 LiCl 0.8197 0.2945 0.5252 -2.395 1.946 NaCl 0.7720 0.2615 0.5105 -3.350 2.818 KCl 0.8161 0.2720 0.5441 -2.358 2.003 PAA/HQ HCl 0.0779 0.4549 0.377 -2.324 1.934 LiCl No well defined peaks NaCl No well defined peaks KCl 0.45 0.488 -0.04 -3.298 1.229 PAA/CAT- HQ HCl 0.5492 0.4476 0.1016 -2.324 1.934 LiCl No well defined peaks NaCl 0.4304 0.2933 0.1371 -2.528 2.874 KCl 0.2369 0.1084 0.1285 -1.002 2.868 Research Journal of Chemical Sciences ___________________________________________________________ ISSN 2231-606XVol. 4(5), 1-9, May (2014) Res. J. Chem. Sci. International Science Congress Association 8 ConclusionThe PAA and the modified PAA were synthesized by oxidative decarboxylation process and they were characterized using different spectroscopic techniques like UV, FT-IR and show the substitution of dihydroxy benzene moieties in the PAA backbone. The thermal study shows that the synthesized polymers were thermally stable and the activation energy confirms the decomposition of the polymers with the same mechanism. The SEM study reveals the micro structured nature of the chemically modified PAA. The CV studies confirm that the chemically modified PAA has well defined voltommogram in acidic medium when compared to the other electrolytes. Reference 1.Hadjichristidis N., Pitsikalis M., Pispas S. and Iatrou H., Polymers with Complex Architecture by Living Anionic Polymerization, Chem. Rev., 101, 3747-3792 (2001)2.Vincent Darcos and David M. Haddleton, Synthesis of ABABA pentablock copolymers via copper mediated living radical polymerization, Eur. Polym. J.,39, 855–862 (2003) 3.Goethals E.J., Dubreuil M., Wang Y., De Witte I., D. Christova, S. Verbrugghe, N. Yanul, L. Tanghe, G. Mynarczuk and F. Du Prez, New polymer architectures by cationic ring-opening polymerization, Macromol. Symp., 153, 209-216 (2000) 4.Davis K.A. and Matyjaszewski K., Synthesis of polymer brushes using atom transfer radical polymerization, Adv. Polym. Sci., 159, 77-88 (2002)5.Hawker C.J., Bosman A.W. and Harth E., Thermal Self-Initiation in Stable Free-Radical Polymerization of styrene,Chem. Rev., 101, 3661-3688 (2001) 6.Perrier S. and Takolpuckdee P., Macromolecular design via reversible addition–fragmentation chain transfer (RAFT)/xanthates (MADIX) polymerization, J. Polym. Sci., Part A: Polym. Chem., 43, 5347-5393 (2005)7.Tyagid D., Hedrick J.L., Webster D.C., Mcgrath J.E. and Wilkes G.L., Structure-property relationships in perfectly alternating segmented poly sulfones/ polydimethylsiloxane copolymer, Polym. J, 29(5), 883-893 (1988)8.Hoogenboom R., Poly (2-oxazoline)s: Alive and Kicking, Macromol.Chem. Phys.,208, 18-25 (2007)9.Burland D.M., Miller R.D. and Walsh C.A., Second order non linearity in poled- polymer systems, Chem. Rev., 94, 31-75 (1994)10.Angiolini L., Benelli T., Giorgini L. and Salatelli E., Synthesis of optically active methacrylic oligomeric models and polymers bearing the side-chain azo-aromatic moiety and dependence of their chiroptical properties on the polymerization degree, Polym. 47, 1875–1885 (2006)11.Rosseinsky D.R. and Mortimer R., Electrochromic Systems and the Prospects for Devicesed, . Adv. Mater,13, 783-793(2001)12.Grote J.G., Zetts J.S., Nelson R.L., Hopkins F.K., Dalton L.R., Zhang C. and Steier W.H., Effect of conductivity and dielectric constant on the modulation voltage for optoelectronic devices based on nonlinear optical polymers, Opt. Eng., 40, 2464-2473 (2001)13.Eugenii Katz and Itamar Willner, A Biofuel Cell with Electrochemically Switchable and Tunable Power Output, J. Am. Chem. Soc., 125, 6803-6813 (2003)14.E. De Giglio E, S. Cometa.S, Cioffi. N, Torsi, L, and Sabbatini, L. Analytical investigations of poly(acrylic acid) coatings electrodeposited on titanium-based implants: a versatile approach to biocompatibility enhancement, Polym. J., 47, 1875–1885 (2006)15.Eyad M. Nawafleh, Tareq T. Bataineh, Muna K. Irshedat, Mahmoud A. Al-Qudah and Sultan T. Abu Orabi Inhibition of Aluminum Corrosion by Salvia Judica Extract Res. J. Chem. Sci., 3(8), 68-72 (2013) 16.Ping-Sheng Liu, Li Li, Ning-Lin Zhou, Jun Zhang, Shao-Hua Wei, Jian Shen. Synthesis and Properties of a Poly(acrylic acid)/ Montmorillonite Superabsorbent Nanocomposite, J. Appl. Polym. Sci., 102, 5725–5730 (2006) 17.Moulay S., Dihydroxy benzene/ benzoquinone containing polymers: organic redox polymer, Actualite Chimique,12, 7-8 (2000)18.Moulay S., Polymers with dihydroxy/dialkoxybenzene moieties, C.R. Chimie, 12, 577-601 (2009) 19.Saravanakumar K. and Kubendran T.R., Density and Viscosities for the Binary Mixtures of 1, 4-Dioxane and Benzene or Chlorobenzene at 303.15, 308.15, 313.15 K and a Pressure of 0.1MPa, Res.J.Chem.Sci.,2(4), 50-56 (2012)50 20.Barbara Mendrek, Barbara Trzebicka, Synthesis and characterization of well-defined poly(tert-butyl acrylate) star polymers Eur. Polym. J, 45, 1979–1993 (2009)21.Mahaveer D., Kurkur, Jae-Rock Lee., Jae Hung Han., and In Lee. 2006. Electroactive behavior of poly (acrylic acid) grafted poly(vinyl alcohol), their synthesis by Ce(IV) glucose redox system and characterization, Smart Mater. Struct.,15(2), 417-423 (2006)22.Singru R.N. Synthesis, characterization and thermal degradation studies of copolymer resins p-cresol-oxamide-formaldehyde,Arch. Appl. Sci. Res., 3(5), 309-325 (2011)23.Anuradha Rangaraj, Veena Vangani, Animesh K Rakshit. Synthesis and Characterization of some Water Soluble Polymers, J. Appl. Polym. Sci.,66, 45–56 (1997) Research Journal of Chemical Sciences ___________________________________________________________ ISSN 2231-606XVol. 4(5), 1-9, May (2014) Res. J. Chem. Sci. International Science Congress Association 9 24.Moulay S. and Mehdaoui R., Hydroquinone/catechol-bearing polyacrylic acid: redox polymer, React. Funct. Poly., 61, 265–275 (2004)25.Richard D. Beaty and Jack D. Kerber, Concepts, Instrumentation and Techniques in Atomic Absorption Spectrophotometry, 2nd ed., pp.1-6. Norwalk, CT: The Perkin-Elmer Corporation (1993)26.Dhanraj T. Masram., Bhave N.S. and Kariya K.P., Synthesis, Characterization and Thermal Degradation Study of Terpolymer-derived from -Hydroxybenzoic Acid, Diaminonaphthelein with Formaldehyde, High Perform. Polym, 22, 1004–1016 (2010)27.William Kemp. Organic Spectroscopy Ed. 3, 60 – 71, Newyork: Palgrave (1991)28.Mustafa aslan Statistical thermodynamics of linear macromolecular structures: a systematic expansion to simha somcynsky lattice hole-Theory, Journal of Naval Science and Engineering., 6 (3), 11-24(2010)29.Yaman boluk and LiyanZhao., Determination of shape nano crystalline cellulose rods International conference on nanotechnology for forest products industry (2009)30.Neeti Sah, Renu Loshali, Rajendra Joshi, Kiran Pandey, Jagdish Prasad and Narain D. Kandpal, Physicochemical studies on nanosized material formed from acrylic acid and poly-di-methylsiloxane polymerization assisted by microwave, Der Chemica Sinica.,3(6), 1421-1427 (2012)31.D. Patidar , D., Rathore, K.S., N. S. Saxen, N.S., Kananbala Sharma, Sharma, T.P. Energy band gap and conductivity measurement of CdSe thin films, chalcogenide letters, 5(2), 21-25 (2008)32.Sailaja G.S., Velayudhan S., Sunny M.C., Sreenivasan K., Varma H.K. and Ramesh P., Hydroxyapatite filled chitosan-polyacrylic acid polyelectrolyte complexes, Journal of materials science, 38, 3653 – 3662 (2003)33.Ferriol M., Gentilhomme A., Cochez N., Oget N. and Mieloszynski J.L., Thermal degradation of poly(methyl methacrylate) (PMMA): modelling of DTG and TG curves, Polym. Degrad. Stab.,79, 271–281 (2003)34.Dharkar K.P., Khamborkar A.K. and Kalambe A.B., Thermal Degradation Analysis of Melamine-Aniline-Formaldehyde Terpolymeric Ligand, Res.J.Chem. Sci., 2(12), 11-16 (2012) 35.Vitaliy V Khutoryanskiy., Maria Grazia Cascone., Luigi Lazzeri., Niccoletta Barbani., Zauresh S Nurkeeva., Grigoriy A Mun., and Artem V Dubolazov. Morphological and thermal characterization of interpolymer complexes and blends based on poly(acrylic acid) and hydroxypropylcellulose, Polym Int.,53, 307–311 (2004)36.Xiao-Dong Fan, You-Lo Hsieh, John M. Krochta, Mark J. Kurth. 2001. Study on Molecular Interaction Behavior, and Thermal and Mechanical Properties of Polyacrylic Acid and Lactose Blends, J. Appl. Polym. Sci. 82, 1921-1927 (2001) 37.Schrebler R., Dell Valle M.E., Gomez H., Veas C. and Cordova R., Preparation of poly thiopene-modified electrodes by electrodeposition of Pt and Pt + Pb. Application to formic acid electro-oxidation, J. Electroanal. Chem., 380, 219-227 (1995)