N, N, N, N-Tetramethylethylenediamine (TMEDA) and 1, 3-Diaminopropane (DAP) as Vapour Phase Corrosion Inhibitor (VPCI) for mild steel under Atmospheric conditions

    ,

Author Affiliations

  • 1Material Sci. & Electrochemistry Lab., Dept of Chem., Ch. Devi Lal University, Sirsa, Haryana – 125055, INDIA
  • 1 Material Sci. & Electrochemistry Lab., Dept. of Chem., Janta Girls College, Ellenabad, Haryana– 125102, INDIA

Res.J.chem.sci., Volume 4, Issue (6), Pages 45-53, June,18 (2014)

Abstract

Industrialization and modernization in now a days has made a strong demand of steel and their maintenance for a strong infrastructure for every country in the race of survival, stabilization, growth and competition. Atmospheric corrosion can aggressively accelerate the rate of degradation of steel during their manufacturing, processing, storage and transportation. In these cases, traditional methods to prevent corrosion are not suitable which provide scope of Vapour Phase Corrosion Inhibitors (VPCI) in industries, defense and daily life. N, N, N, N-Tetramethylethylenediamine (TMEDA) and 1, 3-Diaminopropane (DAP)were investigated as VPCI for mild steel under aggressive corrodents of atmosphere by Weight loss test, Eschke test, Salt spray test, Sulphur dioxide (SO2) test at 50oC and results of these tests were supported by Metallurgical research microscopy technique and SEM technique.

References

  1. Corvo F., Atmospheric Corrosion of Steel in Humid Tropical climates: Humidity, TemperatuSun Radiation, Corros, 40, 4 (1984)
  2. Morcillo M., Chico B., Otero E. and Mariaca L., Effect of Marine Aerosol on Atmospheric Corrosion, 38(4), 24 (1999)
  3. Ericsson R., The influence of SOHumidity on the Atmospheric Corrosion of Steel, Korros., 29, 400 (1978)
  4. Blucher B.D., Lindstrom R., Svensson J.E. and Johansson L.G., The effect of COon the NaClCorrosion of Aluminum, J. Electrochem. Soc.(2001)
  5. Vuorinen E., Ngobeni P., Van der Klashorst G.H., Skinner W., De W.E. and Ernst W.S., Cyclohexylamine and Morpholine as Volatile Corrosion Inhibitors, Brit. Corros. J., 29, 120(1994)
  6. Quraishi M.A., Jamal D. and Singh R.N., Inhibition of Mild Steel Corrosion in the Presence of Fatty Acid Thiosemicarbazides, Corros,, 58 201 (2002)
  7. Subramanian A., Kumar R.R., Natesan M. and Vasudevan T., The Performance of VPI Coated Paper for Temporary Corrosion Prevention of Metals,ACMM, 49 354 (2002)
  8. Subramanian A., Rajendran P., Natesan M., Balakrishnan K., and Vasudevan M., Corrosion Behavior of Metals in SOEnvironment and Its Prevention by Some Volatile Corrosion Inhibitors, ACMM, 46 346 (1999)
  9. Vuorinen E. and Skinner W., Amine Carboxylates as Vapor Phase Corrosion Inhibitors, Brit. Corros. J.,37, 159 (2002)
  10. Skinner W., Preez F.D. and Vuorinen E., Evaluation of Vapor Phase Corrosion Inhibitors, (1999)
  11. Quraishi M.A. and Jamal D., Inhibition of Metals Corrosion by a New Vapor Phase Corrosion Inhibitor, J. , 45 (2005)
  12. Quraishi M.A., Bhardwaj V. and Jamal D., Prevention of Metallic Corrosion by Some Salts of Benzoic Hydrazide under Vapor Phase Conditions, Ind. J. Chem. Tech., 12, 39 (2005)
  13. Zhang D.Q., Gao L.X. and Zhou G.D., Polyamine Compound as a Volatile Corrosion Inhibitor for Atmospheric Corrosion of Mild Steel, Mater. and Corros., 58, 594 (2007)
  14. Khamis E. and Andis N.A., Herbs as New Type of Green, Inhibitors for Acidic Corrosion of Steel, Material Wissenschaft and Werkstoff technik, 33, 550 (2002)
  15. Poongothai N., Rajendran P., Natesan M. and Palaniswamy N., Wood Bark Oils as Vapor Phase Corrosion Inhibitors for Metals in NaCl and SO2 Environments, Ind. J. Chem. Tech., 12, 641(2005)
  16. Premkumar P., Kannan K. and Natesan M., Thyme Extract of Thymus Vulgar L. as Volatile Corrosion Inhibitor for Mild Steel in NaCl Environment, Asian J. Chem., 20, 445 (2008)
  17. Premkumar P., Kannan K. and Natesan M., Natural Thyme Volatile Corrosion Inhibitor for Mild Steel in HCl Environment, J. Metall. and Mater. Sci., 50, 227 (2008)
  18. Cano E., Bastidas D.M., Simancas J. and Bastidas J.M., Dicyclohexylamine nitrite as volatile corrosion inhibitor for steel in polluted environments, Corros.,61, 473 (2005)
  19. Zubielewicz M. and Gnot W., Mechanisms of non-toxic anticorrosive pigments in organic waterborne coatings, Progr. In Organ. Coating.,49, 358 (2004)
  20. Batis G., Kouloumbi N. and Soulis E., Sandblasting: The only way to eliminate rust?, Anti Corros. Meth. and Mat.,45(4), 222 (1998)
  21. Lyublinski E.Y.; Synergistic Corrosion Management Systems for Controlling, Eliminating and Managing Corrosion, WO patent 124058, (2008)
  22. Kumar H., Saini V. and Yadav V., Study of Vapour Phase Corrosion Inhibitors for Mild Steel under different Atmospheric Conditions, Int. J. Engg. & Innovative Tech.,3(3), 206-211 (2013)
  23. Kumar H. and Yadav V., Corrosion Characteristics of Mild Steel under different Atmospheric Conditions by Vapour Phase Corrosion Inhibitors, Am. J. of Materials Sci. & Engg. 1(3), 34-39 (2013)
  24. Kumar H. and Yadav V., CHA, BA, BTA & TEA as Vapour Phase Corrosion Inhibitors for Mild Steel under different Atmospheric Conditions, J. Corros. Sci. & Engg.16, Preprint 4 (2013)
  25. Kumar H. and Saini V., Corrosion characteristics of vapour phase inhibitors for mild steel under different atmospheric condition, J. Corros. Sci. & Engg. 14, Preprint 5 (2012)
  26. Kumar H. and Saini V., DAPA, EA, TU and BI as Vapour Phase Corrosion Inhibitors for Mild Steel under Atmospheric Conditions, Res. J. of Chem. Sciences, 2(2), 10-17 (2012)
  27. Kumar H. and Yadav V., BIA, DPA, MBTA and DMA as Vapour Phase Corrosion Inhibitors for Mild Steel under different Atmospheric Conditions, International Letters of Chemistry, Physics and Astronomy, 52-66 (2014)
  28. Premkumar P., Evaluation of Menthol as Vapour Phase Corrosion Inhibitor for Mild Steel in NaCl Environment, The Arab. J. Sci. Engg.,34(2C), 71 (2009)
  29. Abd S.S., Rehim E., Relay S.A.M., Saleh M.B. and Ahmed R.A., Corrosion Inhibition of Mild Steel in Acidic Medium using 2-amino Thiophenoland 2-Cyanomethyl Benzothiazole, J. Appl. Electrochem., 31(4), 429 (2001)
  30. Quraishi M.A., Sardar R. and Jamal D., Corrosion Inhibition of Mild Steel in HCl by some Aromatic Hydrzides, Mater. Chem. Phys., 71 (3), 30 (2001)
  31. Rajappa S.K. and Venkatesha T.V., New Condensation Products as Corrosion Inhibitors for Mild Steel in an HCl medium, Ind. J. Engg. Mater Sci., 9, 213 (2002)
  32. Quraishi M.A. and Jamal D., Dianils as New and Effective Corrosion Inhibitors for Mild Steel in Acidic Solutions, Mater. Chem. Phys., 78(3), 608 (2003)
  33. Prabhu R.A., Shanbhag A.V. and Venkatesha T.V., Influence of Tramadol [2-[(dimethylamino) methyl]-1-(3-methoxyphenylcyclohexanolhydrate] on corrosion inhibition of mild steel in acidic media, J. App. Electrochem, 37(4), 491 (2007)
  34. Tormoen G.W., Burket J.C., Dante J.F. and Sridhar N., Tri-Service Corrosion conference, (2005)